INTRODUCTION:
Tantalum alloys have long been known to be the most corrosive resistant metal for use in hot acidic environments like hydrochloric, sulfuric, nitric, formic and acetic acid. Its corrosion resistant properties provide multiple benefits for end users including longer equipment life, lower operating downtime and increased operating temperatures.
Tantalum is an excellent material of choice for the fabrication of piping systems, heat exchangers, columns, reactors, bayonet heaters, crucibles, furnace liners and thermocouple protection sheaths; it is also a good choice for the repair of glass lined container s.
Our tantalum products meet the ASTM B521 and B708 standard specifications for tantalum and tantalum alloy seamless and welded tubes as well as plate, sheet and strip.
Material | Forms |
Tantalum | Bar, Rod, Tube, Plate, Sheet, Strip, Foil, Machined Components, Powder |
Ta2.5W | Sheet, Tube, Machined Components |
Ta10W | Billet, Bar, Rod, Tube, Plate, Machined Components |
Ta40Nb | Billet, Bar, Rod, Tube, Plate |
Chemical Compositions(%) | ||||
Element | Tantalum(Unalloyed) | Ta10W | Ta2.5W | Ta40Nb |
C | 0.010 | 0.010 | 0.010 | 0.010 |
O | 0.015 | 0.015 | 0.015 | 0.020 |
N | 0.010 | 0.010 | 0.010 | 0.010 |
H | 0.0015 | 0.0015 | 0.0015 | 0.0015 |
Fe | 0.010 | 0.010 | 0.010 | 0.010 |
Mo | 0.020 | 0.020 | 0.020 | 0.020 |
Nb | 0.100 | 0.100 | 0.100 | 35.0-42.0 |
Ni | 0.010 | 0.010 | 0.010 | 0.010 |
Si | 0.005 | 0.005 | 0.005 | 0.005 |
Ti | 0.010 | 0.010 | 0.010 | 0.010 |
W | 0.05 | 9.0-11.0 | 2.0-3.5 | 0.050 |
Ta | Balanced | Balanced | Balanced | Balanced |
Mechanical Properties for Annealed Plate, Sheet and Strip(Annealed Condition) | ||||
Material |
|
Ultimate Tensile Strength min,psi,(MPa) |
Yield Strength, min, psi (MPa)(2%Offset) |
Elongation, min, % (1-in. Gage Length) |
Tantalum |
T<0.060mm T≥0.060mm |
30 000 (207) 25 000 (172) |
20 000 (138) 15 000 (103) |
20 30 |
Ta10W |
Sheet and Strip Plate |
70 000 (482) 70 000 (482) |
60 000 (414) 55 000 (379) |
15 20 |
Ta2.5W |
T<0.125mm T≥0.125mm |
40 000 (276) 40 000 (276) |
30 000 (207) 22 000 (152) |
20 25 |
Ta40Nb |
T<0.060mm T≥0.060mm |
35 000 (241) 35 000 (241) |
20 000 (138) 15 000 (103) |
25 25 |
Mechanical Requirements for Tantalum and Tantalum Alloy Seamless and Welded Tubes | ||||
|
Tantalum |
Ta2.5W |
Ta10W |
Ta40Nb |
Ultimate tensile strength, min, psi (MPa) |
30 000 (207) |
40 000 (276) |
70 000 (481) |
40 000 (226) |
Yield strength, 0.2% offset, min, psi (MPa) |
20 000 (138) |
28 000 (193) |
60 000 (414) |
28 000 (193) |
Elongation, min, %, in 1 or 2 in. (25 or 51 mm) |
25 |
20 |
15
|
20 |