Our pursuit and enterprise goal is to “Always satisfy our customer requirements”. We keep on to establish and style and design outstanding top quality goods for both our outdated and new prospects and realize a win-win prospect for our clientele likewise as us for Factory Price For Outlets Molybdenum Disilicide U Type Mosi2 Electric Heating Elements, At our firm with high-quality initial as our motto, we manufacture goods that are entirely made in Japan, from materials procurement to processing. This enables them for being used with self-assured peace of mind.
Our pursuit and enterprise goal is to “Always satisfy our customer requirements”. We keep on to establish and style and design outstanding top quality goods for both our outdated and new prospects and realize a win-win prospect for our clientele likewise as us for Molybdenum Disilicide Heater, Mosi2 Heating Elements, U Type Ceramic Electric Heater Rod, We will not only continuously introduce technical guidance of experts from both home and abroad, but also develop the new and advanced products constantly to satisfactorily meet the needs of our clients all over the world.
Molybdenum rods Chemical composition:
| Main and minor components | Min.content(%) | ASTM B386 (361) |
| Mo | 99.95 | balance |
| Impurities | Max.values (μg/g) | Max.values (μg/g) |
| Al | 10 | - |
| Cu | 20 | - |
| Cr | 20 | - |
| Fe | 20 | 100 |
| K | 20 | - |
| Ni | 10 | 50 |
| Si | 20 | 100 |
| W | 300 | - |
| C | 30 | 100 |
| H | 10 | 20 |
| N | 10 | 70 |
| O | 40 | - |
| Cd | 5 | - |
| Hg | 1 | - |
| Pb | 5 | - |
Dimensions and tolerances:
| Diameter (mm) | Diameter tolerance (mm) |
| Ground | |
| 0.50-0.99 | ±0.007 |
| 1.00-1.99 | ±0.010 |
| 1.00-2.99 | ±0.015 |
| 3.00-15.9 | ±0.020 |
| 16.0-24.9 | ±0.030 |
| 25.0-34.9 | ±0.050 |
| 35.0-3939 | ±0.060 |
| ≥40.0 | ±0.20 |
| Cleaned | |
| 0.50-4.0 | ±2.0% |
| 4.10-10.0 | ±1.5% |
| 15.0-50.0 | ±0.30 |
| 51.0-75.0 | ±0.40 |
| 75.1-120.0 | ±1.00 |
| 121.0-165.0 | ±1.50 |
| Turned | |
| 40.0-49.9 | ±0.30 |
| 50.0-165.0 | ±0.40 |
Length and straightness:
| Diameter (mm) | Production length (mm) | Stiraightness/Meter (mm) | |
| Cleaned | Ground/turned | ||
| 0.50-0.99 | ＞500 | ＜2.5 | ＜2.5 |
| 1.00-9.90 | ＞300 | ＜2.0 | ＜1.5 |
| 10.0-165.0 | ＞100 | ＜1.5 | ＜1.0 |
Length tolerance:
| Diameter 0.50-30.0 mm | ||||||
| Nominal length (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | ＞2000 |
| Length tolerance(mm) | ±0.2 | ±0.3 | ±0.5 | ±0.8 | ±1.2 | ±2.0 |
| Diameter ＞30.0 mm | ||||||
| Nominal length (mm) | 6-30 | 30-120 | 120-400 | 400-1000 | 1000-2000 | ＞2000 |
| Length tolerance(mm) | ±1.0 | ±1.5 | ±2.5 | ±4.0 | ±6.0 | ±8.0 |
Density:
1. 00.50-40.0 mm ≥10.15g/cm³
2. 40.1-80.0 mm ≥10.10g/cm³
3. 80.1-120.0 mm ≥10.00g/cm³
4. 120.1-165.0 mm ≥9.90g/cm³
Nondestructive testing: For diameters＞15.00 mm:100% ultrasonic testing; For diameters of 0.50-50.0mm:Eddy curent tests on rods with ground surface.
| Diameter(mm) | Tensile strength(MPa) | 0.2% Yield Strength(MPa) | Elongation(%) | Hardness(HV 10) |
| 0.50-3.18 | ≥585 | ≥450 | ≥15 | |
| 3.18-10.30 | ≥515 | ≥380 | ≥15 | |
| 10.32-22.20 | ≥620 | ≥515 | ≥18 | 230-280 |
| 22.20-28.60 | ≥585 | ≥480 | ≥15 | 225-270 |
| 28.60-47.60 | ≥515 | ≥450 | ≥10 | 215-260 |
| 47.60-73.00 | ≥480 | ≥415 | ≥10 | 210-250 |
| 73.00-88.90 | ≥450 | ≥380 | ≥10 | 205-240 |
| 89.00-120.9 | ≥450 | ≥380 | ≥5 | 200-240 |
| 121.0-164.9 | ≥450 | ≥380 | ≥5 | 180-240 |
| 165.0 | ≥450 | ≥380 | ≥- | 180-240 |
Surface condition:
| Surface： | Cleaned | Ground | Turned |
| φ0.50-165mm | φ0.50-50.00mm | φ≥40.00mm | |
| Roughness | Diameter (mm) | Ra (μm) Ground | Ra (μm) Turned |
| ≤2.50 | ≤0.80 | - | |
| 2.5-50.0 | ≤1.00 | - | |
| ≥40.0 | - | ≤3.2 |